Single Chamber Sintering Furnace For High Termperature Ceramics Sintering

Single Chamber Sintering Furnace For High Termperature Ceramics Sintering

  • High Light

    Single Chamber Ceramics Sinter HIP Furnace

    ,

    380V Sinter HIP Furnace

    ,

    58bar Ceramics Sintering HIP Furnace

  • Usage
    Sintering Furnace,Heat Treatment Furnace,Vacuum Furnace
  • Warranty
    12 Months
  • Weight
    2t-35t
  • Voltage
    220V/380V
  • Temperature Uniformity
    ±5 ℃
  • Degreasant
    PEG, Rubber, Resin
  • Place of Origin
    China
  • Brand Name
    Ruideer
  • Certification
    CE certificate, GB150, JB4732
  • Model Number
    Customizable
  • Minimum Order Quantity
    1 set
  • Price
    USD 93,000-77,000,000
  • Packaging Details
    Special wooden box
  • Delivery Time
    5-8 months
  • Payment Terms
    L/C, T/T
  • Supply Ability
    7 sets / month

Single Chamber Sintering Furnace For High Termperature Ceramics Sintering

10 bar/60bar/100bar Gas Pressure Sintering Furnace-Chinese Reliable Wholesaler--Ruideer 

Technical parameters

 

Service life 6000times / 20-years service life

 

Max. Loading weight

 

≥300kg(According to products and loading space)

 

Max. Designed temp.

 

1600℃(Heating temperature)

 

Max. Working temp.

1550℃

 

Max. working pressure

58bar/98bar

 

Ultimate vacuum degree

1pa (After heating, under cold,empty,dry condition)

 

Pumping speed

 

The vacuum degree is up to 5 Pa within 30min after starting pump. The vacuum degree can reach 3pa after pumping continually within 30min.

Leakage rate (average 24h)

 

2Pa/h(After testing ultimate vacuum,u nder empty cold, clean condition, test in average 24h)

 

Wax-collection rate

 

≥98% (Ar dewaxing with 10kg wax absolutely, average not more than 3 times )

 

Max. Ramp up rate

 

8℃/min(Room temperature ramp up to 1450℃ in vacuum,empty loaded condition,can be soaked in process when 600℃,1000℃ and 1200℃.

≥5℃/min when Fully loaded

 

Cooling time

 

≤6~7h(From 1480℃ drop to 100℃ when fully-loaded,water temperature≤28℃ )

 

UPS time

 

Supply power to indicator and to control furnace when power-off, Keeping time≥80min

 

Temperature uniformity

 

YG8 or YC40 control inserts to test:Magnetic saturation deviation after debinding ≤±0.25%,

Coercivity deviation≤±0.3KA/M

 

Temperature gradient

 

≤±7℃ (Vacuum sinter to 1450℃,Put ceramic FERRO of grade 334 on flat graphite boards(ceramic FERRO supplied by buyer) ,empty condition,can be soak in process,this test result only as reference)
Heating power 280KVA,Suggest user’s inlet wire:≥180mm2

 

Temp.measurement Mode

 

WRe5-26 double-core single thermocouples,mutually redundant,stable and reliable
Temperature control mode 3-zone temp. Control