Zhuzhou Ruideer Metallurgy Equipment Manufacturing Co.,Ltd 86--16673365810 shirley.xiao@zzrde.com
Silicon Nitride Vacuum Annealing Furnace , Hard Alloy High Temperature Vacuum Furnace

Silicon Nitride Vacuum Annealing Furnace , Hard Alloy High Temperature Vacuum Furnace

  • High Light

    vacuum pressure furnace

    ,

    sinter hip furnace

    ,

    Silicon Nitride Vacuum Annealing Furnace

  • Types
    High Temperature Vacuum Furnace​
  • Characteristic
    High Temperature And Pressure
  • Heating Power
    120—600KVA
  • Heating Method
    Graphite Heating
  • Application
    Silicon Nitride
  • Other Name
    High Temperature Vacuum Furnace
  • Place of Origin
    Zhuzhou City, Hunan Province,China
  • Brand Name
    Ruideer
  • Certification
    CE;ISO9001;ISO14001;OHSAS 18001;GB/T29490
  • Minimum Order Quantity
    1set
  • Price
    250000.00——800000.00(USD)
  • Packaging Details
    Special wooden case packing
  • Delivery Time
    60-80 work days
  • Payment Terms
    L/C, T/T
  • Supply Ability
    8 sets/month

Silicon Nitride Vacuum Annealing Furnace , Hard Alloy High Temperature Vacuum Furnace

Silicon nitride, hard alloy high temperature and high pressure gas pressure sintering furnace

 

High Temperature Vacuum Furnace​ Main configuration:

 

◆ Furnace shell: with certificate issued by relevant departments and authorities◆ Furnace door: hydraulic system automatically drives hoop lock

◆ Furnace: high-quality graphite material, graphite particles can be selected by customers

◆ Heater material: isostatic graphite / molded three high graphite

◆ Mafu material: graphite particles can be selected by customers

◆ Material truck: fully automatic loading and unloading trolley

◆ Operation panel: industrial computer / support touch and mouse operation

◆ PLC: Siemens

◆ Thermocouple: Wre5-26 (tungsten sleeve / molybdenum sleeve / ceramic sleeve)

◆ Electrical components: Schneider / Siemens

 

Gas pressure sintering furnaceTemperature and atmosphere uniformity:The magnetic force of the furnace control block is different from that of the cobalt magnetic deviation.Conventional sintering furnace test furnace control block brand isYG6 medium particles, YC40.Debinding pressure sintering integrated.

 

High Temperature Vacuum Furnace​ Technical parameters:

 

 

Specifications RDE-DYL-224 RDE-DYL-336/RDE-DYL-339 RDE-DYL-5512/RDE-DYL-5518 RDE-DYL-5527
Effective space(w* h * l)mm 200*200*400

300*300*600/

300*300*900

500*500*1200/

500*500*1800

500*500*2700
Max.Temperature 1600℃ 1600℃ 1600℃ 1600℃
Maximum load 50Kg 150Kg/200Kg 1200Kg/1500Kg 2000Kg
Vacuum leakage rate:(Average in cold,empty,dry chamber in 3 hours) 1Pa/h 2Pa/h 3Pa/h 3Pa/h
Extreme vacuum 0.8Pa 0.8Pa 1Pa 1.5Pa
Wax-collection rate(negative pressure dewaxing process.The maximum average value is 3 furnaces) 98% 98% 98% 98%
Working pressure

1MPa/2MPa/

6MPa/10MPa

1MPa/2MPa/

6MPa/10MPa

1MPa/2MPa/

6MPa/10MPa

1MPa/2MPa/

6MPa/10MPa

Cooling period(Sintering temperature—100℃) 40min-120min 40min-150min 180min-420min 180min-480min
Temperature control mode Single zone/2-zone 2-zone/3-zone 3-zone/4-zone 4-zone
Atmosphere and temperatureuniformity

Com≤±0.15%

Hc≤±0.25KA/M

Com≤±0.15%

Hc≤±0.25KA/M

Com≤±0.2%

Hc≤±0.3KA/M

Com≤±0.2%

Hc≤±0.3KA/M

Input gas allowed Ar,N2,He,H2,CH4,Co2
Functions:Vacuun dewaxing,H2 dewaxing,vacuum heating,heating with gas mixture(Co2/CH4/H2),heating flowing gas,heating pressure gas,Rapid cooling.

Silicon Nitride Vacuum Annealing Furnace , Hard Alloy High Temperature Vacuum Furnace 0